MECHANICAL SPECIFICATIONS
- Solderability: 90 % coverage after 5 s dip in 235 °C solder following 60 s preheat at 120 °C type R flux dip
- Resistance to Solder Heat: 10 s in 260 °C solder, after preheat and flux per above
- Terminal Strength: 0603: 0.3 kg (0.66 lbs), 0805: 0.6 kg (1.3 lbs), 1206: 1.0 kg (2.2 lbs), 1806: 1.0 kg (2.2 lbs), 1812: 1.5 kg (3.3 lbs) for 30 s
- Beam Strength: 0603: 0.3 kg (0.66 lbs), 0805: 1.0 kg (2.2 lbs), 1206: 2.0 kg (4.4 lbs), 1806: 2.5 kg (5.5 lbs), 1812: 2.5 kg (5.5 lbs)
ENVIRONMENTAL SPECIFICATIONS
- Operating Temperature: - 55 °C to + 125 °C
- Thermal Shock: 100 cycles, - 40 °C to + 125 °C
- Biased Humidity: 85 % RH at 85 °C, 1000 h at full rated current